Productdescriptions: INS-605HEFsubstrate is polyimide with removable siliconeadhesive, suitable for thermal transfer printing of black glossy coated label,is designed for electrical , computer and electronic parts identified with acharacter or barcode label. It is a circuit board in SMT and DIP process duringthe peak of the circuit board attached, can be resistant to various solvents,make sure to maintain superior performance in a variety of extremeenvironments, it is ideal material.
Parameter specifications:
Product structure:
black glossy ink
polyimide film
removable silicone pressure sensitive adhesive
fluorine film
Product features：
features
Test factor
Test method
Test result
thickness
Total thickness
ASTM1000 tset
65±5 um
Coating thickness
20±3um
PI substrate thickness
25±3um
Adhesion thickness
20±5um
adhesion
Paste on stainless steel
Paste 20minutes（ASTM-3330）
≥35N/100mm
Paste 24 hours（ASTM-3330）
≥42N/100mm
Paste on PCB board
Paste 20 minutes（ASTM-3330）
≥25N/100mm
Paste 24 hours（ASTM-3330）
≥40N/100mm
Film thickness
Fluoro-plastic release film
50um±3u transparent
Peel force
Fluoro-plastic release film
15g/25um
Holding tack
Silicone adhesive
5.3N/25mm
Holding power
ASTM D2979 test
Poly ken probe tack 1 second, separate 1 cm per second
≥1000 g
Valid date:
It can storage over 1 year at the condition of unopened at room temperature , below 27℃ and relative humidity of 60% environment.
Notes: Above samples were tested in the performance has not been printed. Below test by Zebra 90xi printer use a sample TR3075 ribbon printed.
Label printed by 3:1 rate barcode ( 6 mil X width barcode), samples influenced by below environment.
Heat resistance
Temperature resistance
Bake 5 minutes in 260℃
No visible impact
Bake 5 seconds in 315℃
No visible impact
Chemical solvents resistance
Solvent resistance performance
1 part IPA，3 parts alcohol without water for 3 minutes.
No visible impact
Terpene flux 3min
No visible impact
10% sodium hydroxide solution 3min
No visible impact
100 o C in deionized water 10 minutes
No visible impact
82 o C with 99% isopropyl alcohol for 10 minutes
No visible impact
Notes：
According to MIL-STD-202G/883E standard, the sample immersed in the specified chemical solvents, then brush lightly 10 times, observe the changes of the surface.
Statement
The above data are based on our generalunderstanding of product features, for general information only, not as a Innovcustomers design and specification basis. Customers who bought this productshould be tested under actual application conditions result from the line todecide whether to apply. Innov warrants to the purchaser of its products inmaterials and good workmanship.