Product descriptions: ：INS-755F-1 substrate is polyimide withremovable silicon adhesive, suitable for thermal transfer printing white mattecoating label, is designed for printed circuit boards orrelated parts designed to identify characters or barcode label material. It isa circuit board in SMT and DIP process during the peak of the circuit board,can be resistant to various solvents, make sure to maintain superiorperformance in a variety of extreme environments.
Parameter specifications:
Product structures：
white ink
Polymide film
removable pressure sensitive adhesive
Fluorine release film
Product features：
features
Test factor
Test method
Test result
thickness
Total thickness
ASTM1000 test
75±5 um
Coating thickness
22±3um
PI substrate thickness
25±3um
Adhesive thickness
25±5um
adhesion
Paste on stainless steel
Paste 20 minutes（ASTM-3330）
≥35N/100mm
Paste 24 hours（ASTM-3330）
≥42N/100mm
Paste on PCB board
Paste 20minutes（ASTM-3330）
≥25N/100mm
Paste 24hours（ASTM-3330）
≥40N/100mm
Film thickness
Fluorine release film
50um±3u transparent
Peel force
Fluorine release film
15g/25um
adhesion
silicone
5.3N/25mm
Holding power
RICOH B 110）或R 6000 ribbon
ASTM D2979 test
Poly ken probe tack 1 second, separate 1 cm per second
≥1000 g
Valid date:
It can storage over 1 year at the condition of unopened at room temperature , below 27℃ and relative humidity of 60% environment.
Notes: Above samples were tested in the performance has not been printed. Below test by Zebra 90xi printer use a sample RICOHB 110C or R6000ribbon printed.
Label printed by 3:1 rate barcode ( 6 mil X width barcode), samples influenced by below environment.
Heat resistance
Temperature resistance
Bake 5 minutes in 260℃
No visible impact
Bake 6 seconds in 315℃
No visible impact
Chemical solvents resistance
Solvent resistance performance
1 part IPA，3 parts alcohol without water for 3 minutes.
No visible impact
Terpene flux 3min
No visible impact
10% sodium hydroxide solution 3min
No visible impact
100 o C in deionized water 10 minutes
No visible impact
82 o C with 99% isopropyl alcohol for 10 minutes.
No visible impact
Notes：
According to MIL-STD-202G/883E standard, the sample immersed in the specified chemical solvents, then brush lightly.
Statement
The above data are based on our generalunderstanding of product features, for general information only, not as a Innovcustomers design and specification basis. Customers who bought this productshould be tested under actual application conditions result from the line todecide whether to apply. Innov warrants to the purchaser of its products inmaterials and good workmanship.